The stress intensity factors for a short crack partially penetrating an inclusion of arbitrary shape

Some approximate solutions for predicting the stress intensity factor of a short crack penetrating an inclusion of arbitrary shape have been developed under mode I and mode II loading conditions. The derivation of the fundamental formula is based on the transformation toughening theory. The transformation strains in the inclusion are induced by the crack-tip field and remotely applied stresses, and approximately evaluated by the Eshelby equivalent inclusion theory. As validated by detailed finite element (FE) analyses, the developed solutions have good accuracy for different inclusion shape and for a wide range of modulus ratio between inclusion and matrix material.     

Residual stresses and transformation toughening in MoSi2 composites reinforced with partially stabilized zirconia

The results of study of the effects of yttria stabilization (0–6 mol.%) on the room-temperature fracture behavior and toughening mechanisms in zirconia-reinforced MoSi₂ are presented in this paper. Transformation toughening is shown to occur only in composites reinforced with zirconia particles stabilized with 2 mol.% yttria. However, the fracture toughness levels are comparable in the other composites with yttria levels between 0 and 6 mol.%. Toughening in the other composites is attributed to the combined effects of residual stress, microcrack shielding/anti-shielding and/or crack deflection. A rigorous micromechanics-based model is presented for the estimation of residual stress levels in brittle materials reinforced with phases that can transform during cooling or under stress. The model is applied successfully to the rationalization of the observed fracture and toughening phenomena.     

Genetically modified starter and protective cultures

Modern approaches towards starter and protective culture improvement rely on advances in molecular biology. For most microorganisms used for food production, gene technological methods have been well developed. By recombinant DNA technology, ‘tailor-made’ starter and protective cultures may be constructed so as to combine technically desirable features. A single strain which normally would fail to accomplish a given ‘wtask’ may now be improved so as to meet a set of requirements necessary for a specific production or preservation process (e.g. wholesomeness, no off-flavour production, overproduction of bacteriocins or particular enzymes). In addition, undesirable properties (e.g. mycotoxin or antibiotic production by cheese moulds) may be eliminated by techniques such as ‘gene disruption’.     

Influence of the Preheat Treatment on the Microstructure and Properties of X37CrMoV5-1 Steel

The technological properties of the hot-work tool steels depend on their microstructural quality induced by the production process and the heat treatment. One of the frequently applied methods to improve microstructure is preheat treatment. The treatment of carbonitriding X37CrMoV5-1 steel has been investigated in fluidized bed furnaces. Thickness and phase composition have been conducted using optical microscopy Neophot 32 and scanning microscopy, JEOL 5400, after etching in nital.     

Improvement in Stress Corrosion Crack Growth Resistance of an Austempered Cast Steel by a Novel Two-Step Austempering Process

An investigation was carried out to examine the influence of microstructure on the stress corrosion cracking (SCC) growth behavior of an austempered high-carbon (1.00%), high-silicon (3.00%), and high-manganese (2.00%) cast steel. Compact tension specimens were prepared from this cast steel as per American Society for Testing Materials standard E-399 and were given four different heat treatments to produce different microstructures. The SCC behavior of these specimens was studied in 3.5% NaCl solution. The test results indicate the K_ISCCvalue of the material increases as the austenite content increases. Significant improvement in SCC resistance was achieved by using a novel two-step austempering process. Intergranular crack growth was observed in all these specimens.     

空间RSCR四杆机构图解综合法的研究

根据空间RSCR四杆机构出现特殊位置的几何特征,运用旋转变换把空间问题转换为平面问题,对实现两特殊位置运动的空间RSCR曲柄摇杆机构的图解综合法进行了探讨。     

油泵柱塞和轴承外套失效分析

对断裂的油泵柱塞、轴承外套从成分、组织、工艺等方面进行了检验分析。结果表明，柱塞首先断裂，断裂后的柱塞碎片卡住了轴承外套，使轴承外套过载脆断。而柱塞的断裂是由于热处理不当，造成淬火加热温度过高，使柱塞的显微组织出现粗大的针状马氏体，并引起淬火裂纹，导致柱塞的韧性下降，脆性增大，随着载荷作用和液压油的渗入，裂纹进一步扩展，当裂纹扩展笃柱塞有效载面积承受不了全部工作应力时，发生脆性断裂。     

Parameters affecting the frequencies of transformation and co-transformation with synthetic oligonucleotides in yeast.

Factors influencing the direct transformation of the yeast Saccharomyces cerevisiae with synthetic oligonucleotides were investigated by selecting for cyc1 transformants that contained at least partially functional iso-1-cytochrome c. Approximately 3 x 10(4) transformants, constituting 0.1% of the cells, were obtained by using 1 mg of oligonucleotide in the reaction mixture. Carrier, such as heterogeneous oligonucleotides, enhanced transformation frequencies. Transformation frequencies were dramatically reduced if the oligonucleotides had a large number of mismatches or had terminally located mismatches. Transformation with oligonucleotides, but not with linearized double-strand plasmid, was efficient in a rad52- strain, suggesting that the pathway for transformation with oligonucleotides is different from that with linearized double-strand plasmid. We describe a procedure of co-transformation with two oligonucleotides, one correcting the cyc1 defect of the target allele in the host strain, and the other producing a desired amino acid alteration elsewhere in the iso-1-cytochrome c molecule; approximately 20% of the transformants obtained by co-transformation contained these desired second alterations.     

Influence of the surface conditions on permeation in the deuterium–MANET system

The condition of the surfaces is of crucial importance for the deuterium permeation through materials. In this work a study of the surface constants for the adsorption (σk₁) and release (σk₂) of deuterium under different surface conditions on the martensitic steel DIN 1.4914 (MANET) has been carried out. The growth of an oxide surface layer (Cr₂O₃) of about 25–30 nm in a MANET sample, heat treated in an oxidizing environment, compared to the bare MANET that have a ‘natural' oxide of about 5 nm has provoked a reduction of both the permeation rate and the recombination coefficient (about 3 orders of magnitude). In addition, the permeation governing process has changed from diffusion-limited to surface-limited. The measurements of the permeation rate of deuterium were performed by a gas-phase permeation technique over the temperature range 574–746 K and for deuterium driving pressures in the range from 3 to 10⁵ Pa.